This work compares the anticorrosive properties of DC electrodeposited CuCoNi, CuCo, and CuNi alloy coatings in a NaCl 0.5 mol L-1 solution. The results showed that j and the bath composition influenced the chemical, morphological, and electrochemical characteristics of the alloy coatings. Among all the studied coatings, the CuCo, CuNi, and CuCoNi ones produced at j = 10 A m-2, j = 60 A m-2, and j = 25 A m-2, respectively, showed the best anticorrosive performances in the saline medium, exhibiting charge transfer resistances (Rtc) higher than 2000 Ω cm2 and an electrical double layer capacitances (Cdl) lower than 8 X10-4 F cm-2. These results agree with the compact morphologies and smaller grain sizes presented by these coatings. Therefore, the anticorrosive properties of the coatings cannot be related only to the less noble metal(s) contents in the alloy but also to their morphologies.

This work proposes the reuse of spent ground coffee waste (SCG) extracts as eco-friendly corrosion inhibitors for carbon steel in acid medium, and the correlation between their anticorrosive efficiency and chemical composition. The extraction method was optimized using a central composite design, and the chemical composition of the extracts was accessed using UV-Vis spectrometry, HPLC, and ICP-OES. EIS and Potentiodynamic Polarization (PP) tests evaluated the anticorrosive properties of the extracts. Total phenol content ranged from 93 mg L-1 to 219 mg L-1 Gallic Acid Equivalent. The highest concentration of phenolic compounds was observed for syringic acid (78.67 mg L-1), while the lowest concentration was verified for (-)-epigallocatechin-3-O-gallate (0.01 mg L-1). The Pearson correlation coefficient showed no correlation between the Rct and the total phenol content, although, positive correlations with the Rct was observed for caffeic acid, (+)-catechin, ferulic acid, and protocatechuic acid. EIS analysis revealed that all of the extracts could act as corrosion inhibitors. The best performance was verified for C3 extract (IE % = 94.83%). PP tests showed that this extract acted as a mixed inhibitor, with a predominant cathodic effect. Therefore, the valorization of the extracts as corrosion inhibitors was successfully achieved.